Сортамент
|
Страна |
Марка изделия |
|||||||
|
Китай |
|
LZHT200 |
LZHT250 |
LZHT300 |
LZQT400-18 |
LZQT450-10 |
LZQT500-7 |
LZQT600-3 |
|
Англия |
|
G1/G2A(NO.30) |
NO.35 |
G2/G2A(NO.45) |
60-40-18 |
66-45-12 |
70-50-05 |
80-55-06 |
|
ЕС |
|
EN-GJL200 |
EN-GJL250 |
EN-GJL300 |
EN GLS 400-18 |
EN GLS 450-10 |
EN GLS 500-7 |
EN GLS 600-3 |
|
Германия |
|
GG20 |
GG25 |
GG30 |
GGG40 |
- |
GGG50 |
GGG60 |
|
Япония |
|
FC200 |
FC250 |
FC300 |
FCD400 |
FCD450 |
FCD500 |
FCD600 |
|
химический состав |
Si |
2.2-2.8 |
2.2-2.6 |
2.2-2.6 |
2.2-2.8 |
2.2-3.2 |
2.2-3.2 |
2.2-3.2 |
|
Mn |
0.3-0.5 |
0.5-0.8 |
0.6-1.2 |
0.1-0.4 |
0.1-0.4 |
0.2-0.5 |
0.3-0.6 |
|
|
P |
≤0.15 |
≤0.15 |
≤0.15 |
≤0.05 |
≤0.05 |
≤0.05 |
≤0.05 |
|
|
S |
≤0.12 |
≤0.12 |
≤0.1 |
≤0.02 |
≤0.02 |
≤0.02 |
≤0.02 |
|
|
C |
2.8-3.8 |
2.8-3.8 |
2.8-3.8 |
3.2-4.0 |
3.2-3.9 |
3.2-3.9 |
3.0-3.8 |
|
|
механические свойства |
|
|
|
|
≥260 |
≥310 |
≥320 |
≥380 |
|
предел текучести |
≥180 |
≥220 |
≥260 |
30≤D≤150≥380; |
30≤D≤150≥420; 150≤D≤450≥400; |
30≤D≤150≥470; 150≤D≤450≥420; |
30≤D≤150≥560; 150≤D≤450≥520; |
|
|
показатель прочности |
|
|
|
30≤D≤120≥18; 125≤D≤600≥15; |
30≤D≤120≥12; 125≤D≤600≥8; |
30≤D≤120≥7; 125≤D≤600≥5; |
30≤D≤120≥3; 125≤D≤600≥2; |
|
|
твердость |
150-180 |
170-220 |
190-240 |
130-170 |
140-200 |
170-230 |
180-250 |
|
|
форма/размер |
круглая форма |
Ф18мм-Ф670мм |
||||||
|
квадратная форма |
25ммх25мм-470ммх470мм |
|||||||
|
прямоугольная форма |
Диагональ 670 мм |
|||||||
|
полукруглая форма |
R30мм – R212мм |
|||||||
Примечание:
1. Данные о химическом составе в таблице приведены только для справки
2. Механические свойства - это результаты экспериментов по отбору образцов тел, круглых на 1/4 диаметра, прямоугольных, квадратных, взятых с 1/4 диагонали
3. Другие марки и состав могут быть изготовлены в соответствии с требованиями заказчика.